石煤灰渣二次焙烧稀酸浸出提钒工艺条件

›› 2010, Vol. 10 ›› Issue (4): 673-678.

石煤灰渣二次焙烧稀酸浸出提钒工艺条件

余德麒施正伦肖文丁李戈跃骆仲泱岑可法

浙江大学能源清洁利用国家重点实验室浙江大学能源清洁利用国家重点实验室上海中电绿科集团公司上海中电绿科集团公司浙江大学能源清洁利用国家重点实验室浙江大学热能工程研究所

收稿日期:2010-04-27 修回日期:2010-06-11 出版日期:2010-08-20 发布日期:2010-08-20
通讯作者: 余德麒

Influential Factors of Vanadium Extraction by Reburning and Dilute Sulfuric Acid Leaching of Ash of Stone Coal

YU De-qi SHI Zheng-lun XIAO Wen-ding LI Ge-yao LUO Zhong-yang CEN Ke-fa

State Key Laboratory of Clean Energy Utilization Zhejiang University State Key Laboratory of Clean Energy Utilization Zhejiang University Shanghai China Electric Green Technology Group Shanghai China Electric Green Technology Group State Key Laboratory of Clean Energy Utilization Zhejiang University State Key Laboratory of Clean Energy Utilization, Zhejiang University

Received:2010-04-27 Revised:2010-06-11 Online:2010-08-20 Published:2010-08-20
Contact: YU De-qi

摘要/Abstract

摘要： 为获得石煤灰渣二次焙烧稀酸浸出提钒工艺的优化条件，对该工艺钒浸出率的影响因素进行了实验研究. 结果表明，二次焙烧温度、二次焙烧时间、熟料粒径、酸浸温度、硫酸浓度5种因素对钒浸出率的影响较大，酸浸液固体积质量比、酸浸时间的影响较小. 最佳工艺条件为：二次焙烧温度850℃，二次焙烧时间1 h，熟料粒径180 mm以下，常温(18℃)酸浸，硫酸浓度0.36 mol/L，液固比2~2.5 mL/g，浸出时间0.25 h. 在此条件下，石煤灰渣钒浸出率可达81%以上.

关键词: 石煤灰渣, 二次焙烧, 稀酸浸出, 影响因素, 钒, 综合利用

Abstract: In order to obtain the optimal conditions of vanadium extraction process by reburning and dilute sulfuric acid leaching of ash of stone coal, the factors affecting the vanadium leaching efficiency were experimentally studied. The results indicated that the reburning temperature, reburning time, particle size of clinker, leaching temperature and concentration of sulfuric acid have obvious influence on the vanadium leaching efficiency, and the ratio of liquid volume to solid mass (L/S) and leaching time affect less. The optimal conditions are obtained as follows: reburning temperature 850℃, reburning time 1 h, particle size of clinker less than 180 mm, leaching temperature 18℃ (room temperature), concentration of sulfuric acid 0.36 mol/L, L/S between 2~2.5 mL/g, and leaching time 15 min. At the conditions, the leaching efficiency of vanadium can reach more than 81%.

Key words: ash of stone coal, reburning, dilute sulfuric acid leaching, influential factor, vanadium, comprehensive utilization

中图分类号:

TF841.3

余德麒施正伦肖文丁李戈跃骆仲泱岑可法. 石煤灰渣二次焙烧稀酸浸出提钒工艺条件[J]. , 2010, 10(4): 673-678.

YU De-qi SHI Zheng-lun XIAO Wen-ding LI Ge-yao LUO Zhong-yang CEN Ke-fa. Influential Factors of Vanadium Extraction by Reburning and Dilute Sulfuric Acid Leaching of Ash of Stone Coal[J]. , 2010, 10(4): 673-678.

[1]	白晨光吕学伟邱贵宝张生富. 攀西钒钛磁铁矿资源高效冶金及清洁提取研究进展[J]. 过程工程学报, 2022, 22(10): 1390-1399.
[2]	宋春光张红玲董玉明裴丽丽刘宏辉江军生徐红彬. 石煤钒矿酸浸尾渣高温焙烧制备陶粒过程元素硫释放规律[J]. 过程工程学报, 2021, 21(2): 167-173.
[3]	张克仑李博魏永刚徐洪傲. 钒铅锌矿硫酸浸出提取钒锌[J]. 过程工程学报, 2021, 21(11): 1297-1303.
[4]	卢伟亮张盈孙沛郑诗礼乔珊张洋李平张懿. 金属钒的制备方法综述[J]. 过程工程学报, 2021, 21(10): 1117-1131.
[5]	王新东李兰杰杜浩赵备备. 亚熔盐高效提钒铬清洁生产技术产业化应用[J]. 过程工程学报, 2020, 20(6): 667-677.
[6]	张菊花梁月张伟薛正良. 钙化-酸浸提钒沉钒母液中锰的回收[J]. 过程工程学报, 2020, 20(10): 1174-1181.
[7]	齐涛王伟菁魏广叶朱兆武曲景奎王丽娜张绘. 战略性稀有金属资源绿色高值利用技术进展[J]. 过程工程学报, 2019, 19(S1): 10-24.
[8]	隋智通娄太平霍守星. 弱氧化剂CO₂(g)对含钒铁水吹炼制钒渣的影响[J]. 过程工程学报, 2019, 19(S1): 45-50.
[9]	王成彦曹志河马保中陈永强. 红土镍矿硝酸加压浸出工艺[J]. 过程工程学报, 2019, 19(S1): 51-57.
[10]	孙朝晖李明高官金李良. 粗四氯化钛有机物精制除钒尾渣提钒技术[J]. 过程工程学报, 2019, 19(S1): 93-98.
[11]	李兰杰赵备备高明磊耿立唐白瑞国柳朝阳王新东. 钒化工冶金固废资源化清洁利用[J]. 过程工程学报, 2019, 19(S1): 99-108.
[12]	魏汝飞陈龙智龙红明王毅璠李家新李亚飞宣明. 铁矿烧结烟气半干法脱硫灰亚临界水热非均相氧化[J]. 过程工程学报, 2019, 19(3): 603-608.
[13]	董虎林包海萍汪浩彭建洪. 磷酸钒锂正极材料掺杂改性研究进展[J]. 过程工程学报, 2019, 19(3): 483-491.
[14]	李崇周俊刘瑶周志茂. 我国废硫酸产生及综合利用现状[J]. 过程工程学报, 2018, 18(S1): 24-34.
[15]	孙昊延朱庆山李洪钟. 钒钛磁铁矿流态化直接还原技术现状与发展趋势[J]. 过程工程学报, 2018, 18(6): 1145-1159.