碱度对含铬型钒钛磁铁矿烧结性能的影响

周密 姜涛 王艳军 杨松陶 张立恒 薛向欣   

  1. 东北大学材料与冶金学院 东北大学材料与冶金学院 东北大学材料与冶金学院 东北大学材料与冶金学院 东北大学材料与冶金学院 东北大学材料与冶金学院
  • 收稿日期:2015-03-09 修回日期:2015-05-04 出版日期:2015-06-20 发布日期:2015-06-20
  • 通讯作者: 薛向欣

Effect of Basicity on Sintering of Cr-bearing Vanadium and Titanium Magnetite Ore

ZHOU Mi JIANG Tao WANG Yan-jun YANG Song-tao ZHANg Li-heng XUE Xiang-xin   

  1. School of Materials and Metallurgy,Northeastern University School of Materials & Matellary, Northeastern University School of Materials and Metallurgy,Northeastern University School of Materials and Metallurgy,Northeastern University School of Materials and Metallurgy,Northeastern University School of Materials and Metallurgy, Northeastern University
  • Received:2015-03-09 Revised:2015-05-04 Online:2015-06-20 Published:2015-06-20
  • Contact: XUE Xiang-xin

摘要: 以承德建龙特殊钢有限公司现场条件为依据,通过烧结杯实验模拟碱度(R)对含铬型钒钛磁铁矿烧结性能的影响,分析了其显微结构. 结果表明,随碱度提高,烧结速度先增大后减小,R=2.5时最大,为19.70 mm/min,烧损增大;R=2.7时转鼓强度最高,为63.53%;碱度提高改善含铬型钒钛烧结矿的低温还原粉化指数(RDI), R=2.7时大于3.15 mm的颗粒的RDI最高,为75.09%;碱度增大生产率先增大后减小,R=2.5时最高,为1.35 t/(m2×h). R=2.1~2.5时燃耗比上升,R=2.1时最低,为43.21 kg/t. 碱度提高有利于提高软化开始和软化终了温度,改善含铬型钒钛烧结矿的软化性能、矿物组成及结构,是其性能改善的内因. 该矿适宜的生产碱度为2.5.

关键词: 含铬型钒钛磁铁矿, 碱度, 烧结, 烧结矿, 转鼓强度, 还原粉化指数

Abstract: The effect of basicity (R) on sintering of Cr-bearing vanadium and titanium magnetite ore was studied via sintering pot experiment on the basis of production conditions in Chengde Jianlong Special Steel Company, and the sinter characterized. The results showed that with the increase of basicity, the sintering rate rose firstly, and then fell with a increasing burning loss, leading to a max sintering rate of 19.70 mm/min at R=2.5. Tumbler strength of sinter had the maximum value was 63.53% when the basicity was 2.7. Meanwhile, increasing the basicity was beneficial to the improvement of low-temperature reduction degradation index (RDI) of sinter, and its maximum value of powders size larger than 3.15 mm was 75.09% at R=2.7. Moreover, with the increase of basicity, productivity rose firstly, then fell, and had a maximum value of 1.35 t/(m2×h) when R=2.5. The fuel consumption ratio rose at R=2.1~2.5, and its minimum value was 43.21 kg/t when R=2.1. In addition, increasing basicity was also beneficial to the softening properties through improving the beginning and ending softening temperatures of sinter. The improvement in mineral composition and structure aroused by increasing the basicity was the essential reason for improving sintering properties. Overall, the optimal basicity of V-Ti-Cr sinter for industrial application was 2.5.

Key words: Cr-bearing vanadium and titanium iron ore, basicity, sintering, sinter, tumbler strength, reduction degradation index