钛铁矿和高磷铁矿混合矿氧气顶吹熔融还原炼铁的工艺条件

›› 2011, Vol. 11 ›› Issue (6): 1024-1029.

钛铁矿和高磷铁矿混合矿氧气顶吹熔融还原炼铁的工艺条件

郈亚丽王华卿山

昆明理工大学冶金与能源工程学院昆明理工大学冶金与能源工程学院昆明理工大学材料与冶金工程学院

收稿日期:2011-09-07 修回日期:2011-11-01 出版日期:2011-12-20 发布日期:2011-12-20
通讯作者: 王华

Smelting Conditions of Reduction Ironmaking from Ilmenite Mixed with High Phosphorus Iron Ore by Top-blown Oxygen

HOU Ya-li WANG Hua QING Shan

Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology Faculty of Metallurgical and Energy Engineering, Kunming University of Science and Technology College of Material and Metallurgy Engineering, Kunming University of Science and Technology

Received:2011-09-07 Revised:2011-11-01 Online:2011-12-20 Published:2011-12-20
Contact: WANG Hua

摘要/Abstract

摘要： 采用氧气顶吹熔融还原法进行了高磷铁矿和钛铁矿混合矿炼铁的实验研究，考察了熔渣四元碱度、反应温度、碳氧摩尔比、通氧时间、保温时间和氧流量对炼铁效果的影响. 结果表明，提高反应温度、在一定范围内增加CaO加入量、提高碳氧摩尔比、延长通氧时间和保温时间、增加氧流量都能不同程度地提高铁还原率. 确定的合理工艺条件为：温度1500℃，碱度1.3，碳氧摩尔比1.0，保温时间30 min，通氧时间10 min，氧流量350 L/h，在此条件下渣铁分离较好，铁还原率达96.17%.

关键词: 高磷铁矿, 钛铁矿, 熔融还原, 炼铁

Abstract: The ironmaking process of oxygen top-blown smelting reduction from high phosphorus iron ore mixed with ilmenite was studied. The experiments were conducted to investigate the effects of slag basicity, temperature, molar ratio of carbon to oxygen, oxygen-blowing time, holding time and oxygen flow rate on iron recovery rate. The experimental results showed that the iron recovery rate increased with increasing of smelting temperature, content of CaO added, molar ratio of carbon to oxygen, oxygen-blowing time, holding time and oxygen flow rate within a certain range. The slag and iron were well separated and iron recovery rate was up to 96.17% under the conditions of holding time of 30 min at 1500℃, slag basicity of 1.3, molar ratio of carbon to oxygen of 1.0, oxygen-blowing time of 10 min and oxygen flow rate of 350 L/h.

Key words: high phosphorus iron ore, ilmenite, smelting reduction, ironmaking

中图分类号:

TF521.6

郈亚丽王华卿山. 钛铁矿和高磷铁矿混合矿氧气顶吹熔融还原炼铁的工艺条件[J]. , 2011, 11(6): 1024-1029.

HOU Ya-li WANG Hua QING Shan. Smelting Conditions of Reduction Ironmaking from Ilmenite Mixed with High Phosphorus Iron Ore by Top-blown Oxygen[J]. , 2011, 11(6): 1024-1029.

[1]	王臻春铁军李东升宁超穆固天朱梦飞龙红明. 高磷铁矿含碳团块直接还原动力学[J]. 过程工程学报, 2018, 18(3): 530-536.
[2]	艾刚华华一新徐存英武腾苏波王运. SiO₂对CaCl₂熔盐电解还原钛铁矿精矿制备FeTi合金的影响[J]. 过程工程学报, 2018, 18(3): 537-543.
[3]	李东升春铁军王臻宁超穆固天朱梦飞龙红明. 高磷铁矿含碳团块直接还原-磁选提铁[J]. 过程工程学报, 2018, 18(2): 375-381.
[4]	李兰杰赵备备王海旭白瑞国陈东辉. 提钒尾渣高效脱碱及配矿炼铁工艺 [J]. , 2017, 17(1): 138-143.
[5]	佟志芳乔家龙陈涛. 炉渣组分对CaO-Al2O3-SiO2-TiO2-MgO-Na2O渣系粘度的影响[J]. 过程工程学报, 2016, 16(2): 189-196.
[6]	李克江张建良张亚鹏刘征建姜曦. 基于节能减排思想分析炼铁工艺的发展[J]. , 2014, 14(1): 162-172.
[7]	付辉龙牛帅陈文彬洪新. 含铬物料铁浴碳氢还原的实验研究[J]. , 2013, 13(2): 246-249.
[8]	魏可卿山王华邓文龙施哲. 富氧顶吹熔融还原高磷铁矿中磷的行为[J]. , 2013, 13(1): 78-82.
[9]	李磊胡建杭王华. 铜渣熔融还原炼铁过程研究[J]. , 2011, 11(1): 65-71.
[10]	尹德友程伟玲谢金印冯孔方王波张捷宇郑少波洪新. 铁浴式熔融还原炉浸入式侧吹对熔池内流动影响的数值分析[J]. , 2010, 10(6): 1066-1070.
[11]	雷鹰李雨彭金辉张利波郭胜惠夏洪应. 机械力对攀枝花钛铁矿结构及反应特性的影响[J]. , 2010, 10(6): 1158-1162.
[12]	梁相博吴潘吕莉梁斌李春. 氧化方式对盐酸浸出攀枝花钛铁矿的影响[J]. , 2010, 10(5): 939-943.
[13]	刘玉民齐涛王丽娜初景龙张懿. KOH亚熔盐法分解钛铁矿[J]. , 2009, 9(2): 319-323.
[14]	马保中王丽娜齐涛冯杨初景龙张懿. 磷酸三丁酯萃取分离钛铁矿亚熔盐反应产物酸解液中Fe3+及金红石型TiO2的制备[J]. , 2008, 8(3): 504-510.
[15]	刘岩;姜茂发;许力贤. 铬矿在CaO-SiO2-MgO-Al2O3渣系中的熔解行为[J]. , 2007, 7(2): 322-326.