摘要: 以温度、时间、搅拌强度为变量,以沉淀率、抽滤后滤饼含水量、烘干后多钒酸铵(APV)中杂质含量等作为评价指标,对酸性铵盐沉钒条件进行了研究. 结果表明:以含钒30 g/L左右的溶液为原料,加硫酸铵后用硫酸调节pH至2.2左右,沸水浴(95℃)中沉淀120 min左右,桨式搅拌转速300 r/min,可获得99%以上的沉淀率,抽滤滤饼含水量20%以下,烘干后APV含Na 0.70%~ 1.08%, S 0.78%~1.20%.
关键词: 多钒酸铵(APV), 酸性铵盐沉淀, 工艺条件
Abstract: The effects of temperature, time, and agitation speed on the acidic precipitation of ammonium polyvanadate from the plant of vanadate-leaching solution were investigated on a laboratory scale. The results show that for the vanadate-leaching solution containing 30 g/L of vanadium, keeping pH about 2.2 at the beginning of precipitation reaction, temperature at about 95oC, agitation speed at 300 r/min, and reaction time being 120 min, could result in the following results: precipitation rate is more than 99%, H2O content in red cake is less than 20%, Na content in dried red cake is between 0.70% and 1.08%, and sulphur content in dried red cake is between 0.78% and 1.02%.
Key words: calcium carbonate, super-fine powder, carbonation method, tube sparger, additive
中图分类号:
TF111
李大标. 酸性铵盐沉钒条件实验研究[J]. , 2003, 3(1): 0-0.
XIANG Lan; XIANG Ying; YUAN Hong-xia; WANG Ting-jie. Preparation of Super-fine Spherical CaCO3 by the Carbonation Method[J]. , 2003, 3(1): 0-0.
0 / / 推荐
导出引用管理器 EndNote|Ris|BibTeX
链接本文: https://www.jproeng.com/CN/
https://www.jproeng.com/CN/Y2003/V3/I1/0