铁矿石粉循环流化床煤基直接还原的实验研究

›› 2011, Vol. 11 ›› Issue (1): 91-96.

铁矿石粉循环流化床煤基直接还原的实验研究

范莉娟吕清刚那永洁于旷世

中国科学院工程热物理研究所中国科学院工程热物理研究所中国科学院工程热物理研究所中国科学院工程热物理研究所

收稿日期:2010-12-06 修回日期:2011-01-20 出版日期:2011-02-20 发布日期:2011-02-20
通讯作者: 范莉娟

Experimental Investigation on Direct Reduction of Iron Ore Powder by Pulverized Coal in a Circulating Fluidized Bed

FAN Li-juan， LU Qing-gang NA Yong-jie YU Kuang-shi,

Institute of Engineering Thermophysics, Chinese Academy of Sciences Institute of Engineering Thermophysics, Chinese Academy of Sciences Institute of Engineering Thermophysics, Chinese Academy of Sciences Institute of Engineering Thermophysics, Chinese Academy of Sciences

Received:2010-12-06 Revised:2011-01-20 Online:2011-02-20 Published:2011-02-20
Contact: FAN Li-juan，

摘要/Abstract

摘要： 在小型循环流化床中对铁矿石粉在氮气气氛下用大同煤粉直接还原进行了实验研究，在800~950℃考察了反应温度对铁矿石粉的还原程度及还原产物微观结构的影响. 结果表明，随反应温度提高，铁矿石粉还原产物的金属化率及还原度均增加，800~850℃时增幅较大，850~900℃时增幅平缓，900~950℃时又出现较大增幅，950℃时达到63%的金属化率和87%的还原度；与还原前的铁矿石粉相比，还原产物的比表面积和总孔体积在800℃时均增加，而在其他温度时均减小，对应的平均孔径变化规律则相反.

关键词: 铁矿石粉, 循环流化床, 煤基还原

Abstract: The effect of reaction temperature on the reduction degree and microscopic structure of reduced products, and the reduction process of iron ore powder by Datong pulverized coal in nitrogen was examined in a circulating fluidized bed in the reaction temperature range from 800℃ to 950℃. The metallization and reduction degrees of reduced products increase as the reaction temperature increases. There is a larger increase at 800~850℃, moderate increase at 850~900℃ and the greater increase at 900~950℃. The metallization and reduction degrees can reach 63% and 87%, respectively, when the reaction temperature ascends to 950℃. Compared with the raw iron ore powder, the specific surface area and total pore volume of reduced products are increased at 800℃, while reduced at the other temperatures, the corresponding variation of the average pore size parameters is opposite.

Key words: iron ore powder, circulating fluidized bed, coal-based reduction

中图分类号:

TF559

范莉娟吕清刚那永洁于旷世. 铁矿石粉循环流化床煤基直接还原的实验研究[J]. , 2011, 11(1): 91-96.

FAN Li-juan; LU Qing-gang NA Yong-jie YU Kuang-shi;. Experimental Investigation on Direct Reduction of Iron Ore Powder by Pulverized Coal in a Circulating Fluidized Bed[J]. , 2011, 11(1): 91-96.

[1]	徐文青黄学静谢军朱廷钰. 含内构件的循环流化床的动态压力特性[J]. 过程工程学报, 2018, 18(6): 1267-1275.
[2]	庄煌煌何宏舟李志伟邹峥. 粒径对福建无烟煤在CFB锅炉中燃尽的影响[J]. , 2013, 13(5): 846-850.
[3]	姚常斌汪印董利别如山许光文. 白酒糟双床解耦燃烧模拟实验研究[J]. , 2011, 11(2): 283-288.
[4]	纪文峰董利汪印聂伟许光文. 循环流化床煤热解拔头工艺循环颗粒流分配[J]. , 2010, 10(2): 215-220.
[5]	王向辉;高士秋;宋文立;许友好;张久顺. 操作条件对双循环回路变径提升管压降的影响[J]. , 2006, 6(6): 872-877.
[6]	张少峰;王琦;高川博;刘燕. 液固两相外循环流化床压力波动信号的统计及频谱分析[J]. , 2006, 6(6): 878-883.
[7]	张磊;杨学民;谢建军;丁同利;姚建中;宋文立;林伟刚. 循环流化床燃煤过程NOx和N2O产生-控制研究进展[J]. , 2006, 6(6): 1004-1010.
[8]	常培廷;胡刚石;韩明汉;吴勤;魏飞;金涌. 两段循环流化床中氯化氢催化氧化制氯气[J]. , 2006, 6(1): 47-50.
[9]	王杰广;吕雪松;姚建中;林伟刚;都林. 下行床煤拔头工艺的产品产率分布和液体组成[J]. , 2005, 5(3): 241-245.
[10]	王维;卢旭晨;李佑楚. 循环流化床燃烧器的一维拟流体数值模拟[J]. , 2004, 4(5): 385-390.
[11]	段文立;宋文立;罗灵爱. 两段循环流化床吸附有机气体实验[J]. , 2004, 4(3): 210-214.
[12]	童华;李洪钟. 在具有锥形料腿的循环流化床中流化CaCO3超细颗粒[J]. , 2004, 4(3): 204-209.
[13]	魏耀东;刘仁桓;孙国刚;时铭显. 负压差立管气固流动的不稳定性实验分析[J]. , 2003, 3(6): 493-497.
[14]	魏耀东;刘仁桓;孙国刚;时铭显. 负压差立管内气固两相流的流态特性及分析[J]. , 2003, 3(5): 0-0.
[15]	李晓祥;石炎福;黄卫星;余华瑞;祝京旭. 气固循环流化床颗粒浓度波动信号的预测[J]. , 2003, 3(1): 0-0.