AgBr纳米颗粒和纳米线的微乳合成

周海成，徐晟，李亚栋   

  1. 1. 清华大学化学系，北京 100084； 2. 山东理工大学化学工程学院，山东 淄博 255000
  • 出版日期:2003-06-20 发布日期:2003-06-20

Electrodeposited Ultrafine Metal Particles in Pores of Porous Anodic Films of Aluminum

LI Ling-chuan, LU Li-zhu, ZHANG Yi   

  1. 1. Department of Chemistry, Tsinghua University, Beijing 100084, China; 2. College of Chemical Engineering, Shandong University of Technology, Zibo, Shangdong 255000, China
  • Online:2003-06-20 Published:2003-06-20

PDF

摘要： 在环己烷/Triton X-100/正戊醇/水相的微乳体系中，合成了均一的AgBr纳米颗粒. 改变反应物的浓度，得到了AgBr的纳米线. 利用透射电子显微镜(TEM)对产物进行表征，并初步探讨了反应条件对于产物形貌的影响.

关键词: 微乳液, AgBr纳米颗粒, AgBr纳米线

Abstract: Uniform AgBr nanoparticles were prepared in microemulsions containing cyclohexane, Triton X-100, n-pentanol and aqueous solution. By changing the reactant molar ratios, AgBr nanowires were obtained in this system. Transmission electron microscopy（TEM）was utilized to characterize the morphology of AgBr products. It is found that reactant molar ratio has important influence on the shape of final products.