摘要: 报道了硫杆菌在3种不同方式下浸出低品位镍铜硫化矿的实验结果. 采用通气气搅浸出,在15%矿浆浓度下,浸出20 d后,镍、铜、钴浸出率可分别达到95.4%, 48.6%和82.6%;采用通气搅拌浸出,在25%的矿浆浓度下,浸出14 d后,镍、铜、钴浸出率分别为80.2%, 45.2%和78.4%. 采用柱式渗滤浸出,在液固比为40:1情况下,浸出49 d后,镍、铜、钴浸出率分别为48.5%, 37.5%和33.6%.
关键词: 生物浸出, 氧化亚铁硫杆菌, 氧化硫硫杆菌, 低品位镍铜硫化矿
Abstract: Bioleaching of Ni, Cu and Co from the Jinchuan low-grade Ni–Cu–Co sulfide ore has been investigated with aerated leaching, agitated leaching with air bubbling, and column leaching respectively. The highest recovery was achieved in the aerated leaching. Leaching 20 d with pulp density of 15%, the leached Ni, Cu and Co were 95.4%, 48.6% and 82.6% respectively. By agitated leaching with air bubbling for 14 d at the pulp density of 25%, the leached Ni, Cu and Co were 80.2%, 45.2% and 78.4% respectively. With column leaching for 49 d, the leached Ni, Cu and Co were 48.5%, 37.5% and 33.6% respectively.
Key words: bioleaching, Thiobacillus ferrooxidans, Thiobacillus thiooxidans, low-grade Ni–Cu sulfide ore
中图分类号:
TF803.21
陈泉军;方兆珩. 生物浸出低品位镍铜硫化矿中的镍、铜、钴[J]. , 2001, 1(4): 0-0.
CHEN Quan-jun; FANG Zhao-heng. Boileaching of Ni, Cu and Co from a Low-grade Ni–Cu Sulfide Ore[J]. , 2001, 1(4): 0-0.