石煤钒矿拌酸熟化浸出新工艺

›› 2013, Vol. 13 ›› Issue (2): 202-206.

石煤钒矿拌酸熟化浸出新工艺

万洪强宁顺明佘宗华邢学永封志敏

长沙矿冶研究院有限责任公司长沙矿冶研究院有限责任公司长沙矿冶研究院有限责任公司长沙矿冶研究院有限责任公司长沙矿冶研究院有限责任公司

收稿日期:2013-01-05 修回日期:2013-02-20 出版日期:2013-04-20 发布日期:2013-04-20
通讯作者: 万洪强

New Extraction Process of Vanadium from Stone Coal by Acid Curing

WAN Hong-qiang NING Shun-ming SHE Zong-hua XING Xue-yong FENG Zhi-min

Changsha Research Institute of Mining and Metallurgy Co.,Ltd Changsha Research Institute of Mining and Metallurgy Co.,Ltd Changsha Research Institute of Mining and Metallurgy Co.,Ltd Changsha Research Institute of Mining and Metallurgy Co.,Ltd Changsha Research Institute of Mining and Metallurgy Co.,Ltd

Received:2013-01-05 Revised:2013-02-20 Online:2013-04-20 Published:2013-04-20
Contact: WAN Hong-qiang

摘要/Abstract

摘要： 对南方某石煤钒矿进行拌酸熟化浸出，考察了矿物粒度、加水量、硫酸用量、熟化温度、熟化时间及水浸工艺参数对钒浸出的影响，并研究了H2O在熟化过程中的行为. 得到最佳工艺流程和结果为：先将石煤钒矿磨至125 mm以下，加10%水润湿，再加入20%浓硫酸拌匀，140℃下保温熟化3 h，按液固比1.5 mL/g水浸2 h，钒浸出率达87.8%. 石煤矿物中含钒云母结构在熟化过程中被破坏，形成难溶的SiO2，浸出液中SiO2浓度为0.09 g/L，利于后续处理.

关键词: 浸出, 石煤, 拌酸熟化, 钒

Abstract: Using the vanadium-containing stone coal from south China as raw material, the acid curing process of vanadium recovery was studied. The effects of process parameters, such as granularity, water addition, dosage of sulfuric acid, curing temperature, curing time and leaching solution, on the leaching of vanadium were examined, as well as the behavior of H2O in the acid curing process. The optimal conditions were obtained as follows: ore granularity 125 mm, water addition 10%(w), dosage of sulfuric acid 20%(w), curing temperature 140℃, curing time 3 h, leaching time 2 h, and ratio of liquid to solid 1.5 mL/g. Under the optimum conditions, the leaching rate of vanadium was 87.8%. The structure of micas mineral in the ore was destroyed, and SiO2 formed in the curing, which was difficult to digest. The concentration of SiO2 in leaching solution was 0.09 g/L, being beneficial to subsequent processing.

Key words: leaching, stone coal, acid curing, vanadium

中图分类号:

TF841.3

万洪强宁顺明佘宗华邢学永封志敏. 石煤钒矿拌酸熟化浸出新工艺[J]. , 2013, 13(2): 202-206.

WAN Hong-qiang NING Shun-ming SHE Zong-hua XING Xue-yong FENG Zhi-min. New Extraction Process of Vanadium from Stone Coal by Acid Curing[J]. , 2013, 13(2): 202-206.

[1]	张广安张福元. 火试金灰皿在乙酸-H₂O体系中铅的浸出动力学[J]. 过程工程学报, 2022, 22(6): 774-781.
[2]	周育生邱冠周景建发郑富强王帅陈凤郭宇峰. 改性电炉钛渣矿相解构法制备富钛料新工艺研究[J]. 过程工程学报, 2022, 22(5): 651-659.
[3]	饶富郑晓洪张西华陶天一曹宏斌吕伟光孙峙. MOCVD生产废料中镓、铟提取工艺及其动力学研究[J]. 过程工程学报, 2022, 22(5): 689-698.
[4]	孙思涵潘福生谢勇冰曹宏斌张懿. 化学氧化强化湿法冶金清洁生产：进展与展望[J]. 过程工程学报, 2022, 22(2): 145-161.
[5]	沈蔡龙贾炎陈彦臻张广积杨超. 化工技术在生物冶金过程强化中的研究进展[J]. 过程工程学报, 2022, 22(10): 1349-1359.
[6]	白晨光吕学伟邱贵宝张生富. 攀西钒钛磁铁矿资源高效冶金及清洁提取研究进展[J]. 过程工程学报, 2022, 22(10): 1390-1399.
[7]	宋春光张红玲董玉明裴丽丽刘宏辉江军生徐红彬. 石煤钒矿酸浸尾渣高温焙烧制备陶粒过程元素硫释放规律[J]. 过程工程学报, 2021, 21(2): 167-173.
[8]	张克仑李博魏永刚徐洪傲. 钒铅锌矿硫酸浸出提取钒锌[J]. 过程工程学报, 2021, 21(11): 1297-1303.
[9]	卢伟亮张盈孙沛郑诗礼乔珊张洋李平张懿. 金属钒的制备方法综述[J]. 过程工程学报, 2021, 21(10): 1117-1131.
[10]	叶劲松陈天虎唐梦娟李玉晖卫新来金杰吴克. 硫铁矿尾矿中铜的硫酸浸出[J]. 过程工程学报, 2020, 20(9): 1053-1062.
[11]	付云枫王玮玮. 从熔盐电解废渣中回收钪和氟[J]. 过程工程学报, 2020, 20(8): 929-937.
[12]	王新东李兰杰杜浩赵备备. 亚熔盐高效提钒铬清洁生产技术产业化应用[J]. 过程工程学报, 2020, 20(6): 667-677.
[13]	任坤马淑花刘福立李军王晓辉. 褐煤粉煤灰中汞的赋存状态[J]. 过程工程学报, 2020, 20(4): 418-423.
[14]	焉杰文李彬潘德安. 超声强化在湿法浸出过程中的应用[J]. 过程工程学报, 2020, 20(11): 1241-1247.
[15]	龚傲吴选高喻小强王定纯徐志峰田磊. 选择性还原氨浸从高硅低品位铜钴矿中提取铜、钴的工艺及其浸出动力学[J]. 过程工程学报, 2020, 20(10): 1156-1165.