二氧化碳活化法制备高比表面积碳气凝胶

侯今强,沈军,薛辉,吴广明,周斌,倪星元   

  1. 上海,同济大学波耳固体物理研究所
  • 出版日期:2005-12-20 发布日期:2005-12-20

Preparation of High Specific Surface Area Carbon Aerogels via CO2 Activation

HOU Jin-qiang,SHEN Jun,XUE Hui,WU Guang-ming,ZHOU Bin,NI Xin-yuan   

  1. Pohl Institute of Solid State Physics, Tongji University, Shanghai
  • Online:2005-12-20 Published:2005-12-20

摘要: 以间苯二酚-甲醛为原料,常压干燥条件下制备传统的碳气凝胶,通过活化工艺成功地将其比表面积提高了3倍以上. 用比表面积测试及孔径分布、扫描电镜(SEM)等手段对其微观结构进行了表征并优化了工艺参数.

关键词: 碳气凝胶, 常压干燥, 活化

Abstract: Carbon aerogels were synthesized from sol-gel polymerization of resorcinol-formaldehyde and dried under ambient pressure and room temperature. The specific surface area of carbon aerogels after the CO2 activation would be three times larger than that of normal ones. The microstructures of carbon aerogels were investigated by scanning electron microscope (SEM) and specific surface area measurement, and the process parameters were optimized.

Key words: carbon aerogles, ambient drying process, activatio