Abstract: TiO2/C particles as photocatalyst were prepared by dipping TiO2 suspension solution with activated carbon and were applied in the photocatalytic-electrocatalytic degradation of phenol, the Ti/SnO2+Sb2O3/PbO2 electrode and oxygen diffusion electrode were used as anode and cathode respectively, and a 250 W ultraviolet lamp (365 nm) as side light source. The SEM results of TiO2/C and Ti/SnO2+Sb2O3/PbO2 anode indicated that the TiO2 on carbon particles was uniform and PbO2 film on the surface of anode was in cauliflower form, the XRD result of oxygen diffusion electrode showed that only crystalline graphite was found. The influential parameters of degradation process such as applied cell voltage (E), initial concentration of phenol (C0), amount of TiO2 catalyst and air flow rate (v) were discussed. Under the following experimental conditions of C0=50 mg/L, pH=6, E=2 V, TiO2 0.98 mg/mL, v=382.2 mL/min, and light intensity I=10.5 mW/cm2, phenol could be entirely degraded, and about 89% of total organic carbon (TOC) was removed after 3 h degradation.

Key words: interactive oxidation, photocatalysis and electrocatalysis, TiO2/C, phenol

摘要： TiO2/C particles as photocatalyst were prepared by dipping TiO2 suspension solution with activated carbon and were applied in the photocatalytic-electrocatalytic degradation of phenol, the Ti/SnO2+Sb2O3/PbO2 electrode and oxygen diffusion electrode were used as anode and cathode respectively, and a 250 W ultraviolet lamp (365 nm) as side light source. The SEM results of TiO2/C and Ti/SnO2+Sb2O3/PbO2 anode indicated that the TiO2 on carbon particles was uniform and PbO2 film on the surface of anode was in cauliflower form, the XRD result of oxygen diffusion electrode showed that only crystalline graphite was found. The influential parameters of degradation process such as applied cell voltage (E), initial concentration of phenol (C0), amount of TiO2 catalyst and air flow rate (v) were discussed. Under the following experimental conditions of C0=50 mg/L, pH=6, E=2 V, TiO2 0.98 mg/mL, v=382.2 mL/min, and light intensity I=10.5 mW/cm2, phenol could be entirely degraded, and about 89% of total organic carbon (TOC) was removed after 3 h degradation.

关键词: interactive oxidation, photocatalysis and electrocatalysis, TiO2/C, phenol