摘要: 以硫酸盐为原料,添加NaOH溶液和NaHCO3粉末,先制备碱式碳酸盐前驱体,350℃空气中焙烧1 h后,制备出复合锌镍铁氧体纳米晶体. 经XRD和TEM分析,粒径约为30 nm,粒度较均匀. 通过改变原料中锌盐与镍盐的配比,制备出Zn0.9Ni0.1Fe2O4, Zn0.8Ni0.2Fe2O4, Zn0.7Ni0.3Fe2O4, Zn0.6Ni0.4Fe2O4和Zn0.5Ni0.5Fe2O4 五种纳米粉.
关键词: 复合锌镍铁氧体, 纳米粉体, 制备实验
Abstract: ZnxNi1-xFe2O4 nanosized powders were prepared by calcined basic carbonate precursor synthesized from solid FeSO4×7H2O, NiSO4×6H2O, ZnSO4×7H2O, NaHCO3 salts and concentrated NaOH solution, then the precursor was calcined at 350oC for 1 h. The microstructure of the obtained sample was examined by XRD and TEM analyses. The results show that the size of nanocrystalites is about 30 nm. Changing proportion of ZnSO4×7H2O and NiSO4×6H2O, nanocrystalline Zn0.9Ni0.1Fe2O4, Zn0.8Ni0.2Fe2O4, Zn0.7Ni0.3Fe2O4, Zn0.6Ni0.4Fe2O4 and Zn0.5Ni0.5Fe2O4 were also prepared.
Key words: ZnxNi1-xFe2O4, nanosized powder, preparation experiment
中图分类号:
TM277.1
朱伟长;阎勇;丁飞. 复合锌镍铁氧体纳米粉体材料的制备实验[J]. , 2002, 2(6): 0-0.
ZHU Wei-chang; YAN Yong; DING Fei. Preparation Experiment on Nanosized ZnNi Ferrite Powders[J]. , 2002, 2(6): 0-0.
0 / / 推荐
导出引用管理器 EndNote|Ris|BibTeX
链接本文: https://www.jproeng.com/CN/
https://www.jproeng.com/CN/Y2002/V2/I6/0