PTFE-PPS复合超疏水涂层的制备与表征

王浩,王昌松,陈颖,冯新,陆小华   

  1. 南京工业大学化学化工学院
  • 出版日期:2007-06-20 发布日期:2007-06-20

Preparation and Characterization of Superhydrophobic PTFE-PPS Composite Coating

WANG Hao,WANG Chang-song,CHEN Ying,FENG Xin,LU Xiao-hua   

  1. College of Chemistry and Chemical Engineering, Nanjing University of Technology
  • Online:2007-06-20 Published:2007-06-20

PDF

摘要： 通过喷涂工艺在铝基片表面制备出聚四氟乙烯(PTFE)-聚苯硫醚(PPS)复合超疏水涂层，该复合涂层具有与荷叶表面类似的二次结构，与水的静态接触角为155o，滚动角为7o. 与纯PTFE超疏水涂层相比，PTFE涂层中引入PPS后，涂层的粘附力从5级提高到1级，铅笔硬度从4B提高到4H，柔韧性从(10±0.1) mm提高到(1±0.1) mm，可以更好地满足工业应用要求.

关键词: 聚四氟乙烯, 聚苯硫醚, 超疏水, 复合涂层

Abstract: The superhydrophobic polytetrafluoroethylene-polyphenylene sulfide (PTFE-PPS) composite coating was prepared by spraying coating on the aluminum substrate. Scanning electron microscopy (SEM) investigation indicated that the composite coating had the similar surface structure to that of lotus leaf. The water contact angle on the coating surface was 155o and the sliding angle was 7o. Compared with the pure superhydrophobic PTFE coating on the aluminum substrate, the conglutination force of the composite coating was improved from grade 5 to grade 1, the pencil rigidity was increased from 4B to 4H, and the flexility of the composite coating was improved from (10±0.1) mm to (1±0.1) mm. The composite coating was sufficient to the requirements of industrial application.

Key words: polytetrafluoroethylene, polyphenylene sulfide, superhydrophobic, composite coating