污泥-锯末混合ZnCl2活化制备活性炭

doi:10.12034/j.issn.1009-606X.217400

过程工程学报 ›› 2018, Vol. 18 ›› Issue (4): 792-798.DOI: 10.12034/j.issn.1009-606X.217400

污泥-锯末混合ZnCl₂活化制备活性炭

吴东强1，马培勇2,3*，胡淞4，邢献军2,3，张贤文1,3

1. 合肥工业大学汽车与交通工程学院，安徽合肥 230009
2. 合肥工业大学机械工程学院，安徽合肥 230009
3. 合肥工业大学先进能源技术与装备研究院，安徽合肥 230009
4. 安徽省环境保护产业发展促进会，安徽合肥 230000

收稿日期:2017-11-16 修回日期:2018-01-16 出版日期:2018-08-22 发布日期:2018-08-15
通讯作者: 马培勇 mapeiyong@163.com
基金资助:
国家自然科学基金项目

Preparation of activated carbon from sludge and sawdust with ZnCl₂ as activator

Dongqiang WU1, Peiyong MA2,3*, Song HU4, Xianjun XING2,3, Xianwen ZHANG1,3

1. School of Automobile and Transportation Engineering, Hefei University of Technology, Hefei, Anhui 230009, China
2. School of Mechanical Engineering, Hefei University of Technology, Hefei, Anhui 230009, China
3. Institute of Advanced Energy Technology & Equipment, Hefei University of Technology, Hefei, Anhui 230009, China
4. Anhui Province Environmental Protection Industry Development Association, Hefei, Anhui 230000, China

Received:2017-11-16 Revised:2018-01-16 Online:2018-08-22 Published:2018-08-15
Contact: Peiyong Ma mapeiyong@163.com

摘要/Abstract

摘要： 以城市污水厂二沉池污泥为主要原料、固体ZnCl2为活化剂，添加一定量锯末，在高温管式炉中采用化学活化法制备污泥活性炭，通过单因素实验考察了锯末添加率、盐料比、活化温度、活化时间对污泥活性炭吸附性能的影响. 结果表明，锯末添加量为20%、盐料质量比为2.0、活化温度为550℃、活化时间为15 min时，所得活性炭碘吸附性能最优，达679.25 mg/g；污泥活性炭具有发达的孔结构，其比表面积达609.68 m2/g，总孔容为0.51 cm3/g，平均孔径为3.51 nm.

关键词: 污泥, 活性炭, 氯化锌, 干混, 制备, 吸附, 孔隙结构

Abstract: The sludge based activated carbon was prepared by activation of ZnCl2 in a pyrolytic furnace with the sludge from municipal wastewater treatment plants and sawdust. And single factor experiments were conducted to explain the effects of four factors, sawdust addition rate, material salt ratio, activation temperature and activation time, on the adsorption performance of sludge activated carbon. The results showed that the optimum adsorption capacity of activated carbon can reach 679.25 mg/g when the mass fraction of the sawdust in the mixture 20%, the material/salt mass ratio of 2, the activation temperature of 550℃ and the activation time of 15 min, respectively. The sludge activated carbon has developed pore structure, the specific surface area up to 609.68 m2/g, the total pore volume comes to 0.51 cm3/g, and the average pore size is 3.51 nm.

Key words: sludge, activated carbon, zinc chloride, dry mixing, preparation, absorption, pore structure

吴东强马培勇胡淞邢献军张贤文. 污泥-锯末混合ZnCl₂活化制备活性炭[J]. 过程工程学报, 2018, 18(4): 792-798.

Dongqiang WU Peiyong MA Song HU Xianjun XING Xianwen ZHANG. Preparation of activated carbon from sludge and sawdust with ZnCl₂ as activator[J]. Chin. J. Process Eng., 2018, 18(4): 792-798.

参考文献

[1]. 苏铭华. 污泥质废弃物衍生燃料的研制开发[J]. 中国资源综合利用, 2009, 27(07): 14-15. [2017-08-21].
SU M H. Research and development of sludge derived fuel [J]. China Resources Comprehensive Utilization, 2009, 27 ( 7) : 14-15 ( in Chinese).
[2]. 赵丽君, 张大群, 陈宝柱. 污泥处理与处置技术的进展[J]. 中国给水排水, 2001, 17( 6): 23-25.
ZHAO L J, ZHANG D J, CHEN B Z. Advances in sludge treatment and disposal technology [J]. China Water and Wastewater, 2001, 17( 6): 23-25.
[3]. 刘英华. 城市污水处理厂污泥制备活性炭的研究[D]. 南京理工大学, 2008.
LIU Y H. Study on Preparation of activated carbon from sewage sludge from municipal wastewater treatment plant [D]. Nanjing University of Science and Technology, 2008.
[4]. 夏莉. 微波热解污泥及其产物组成的分析[D]. 大连理工大学, 2008.
XIA L. Analysis of microwave pyrolysis sludge and its product composition [D]. Dalian University of Technology, 2008.
[5]. MOHAMMED R, IMITRI M, OUCHRA B, et al. In-vessel treatment of urban primary sludge by aerobic composting [J]. Bioresource Technology, 2010, 101( 15) : 5988-5995．
[6]. 任爱玲,王启山,贺君. 城市污水处理厂污泥制活性炭的研究[J]. 环境科学, 2004,5( 增刊 1): 48-51.
REN A L, WANG Q S, HE J. Study on the activated carbon produced with sewage sludge [J]. Environmental Science, 2004, 5 (suppl 1 ) : 48-51.
[7]. 李依丽,王姚,李利平,等. 污泥活性炭的制备及其性能的优化[J]. 北京工业大学学报, 2013, 39 (03): 452-458. [2017-08-21].
LI Y L, WANG Y, LI L P, et al. Preparation of activated carbon from sewage sludge and optimization of its performance [J]. Journal of Beijing University of Technology, 2013, 39 (03): 452-458. [2017-08-21].
[8]. 李依丽, 李利平, 尹晶, 等. 污泥基活性炭的两步热解优化制备及其性能表征[J]. 北京工业大学学报,2013, 39 (12): 1887-1890. [2017-08-21].
LI Y L, LI L P, YIN J, et al. Preparation and characterization of activated carbon from sewage sludge by two steps pyrolysis [J]. Journal of Beijing University of Technology, 2013, 39 (12): 1887-1890. [2017-08-21].
[9]. LI Y L, LI Y L, LI L P, et al. Preparation and analysis of activated carbon from sewage sludge and corn stalk[J]. Advanced Powder Technology, 2016, 27 (2): 684-691.
[10]. 李道静,封莉,张立秋. 玉米芯掺杂对污泥基活性炭性能的影响[J]. 环境工程学报, 2012, 6(03): 1010-1014. [2017-08-21].
LI D J, FENG L, ZHANG L Q, Effect of corncob blending on properties of sludge based activated carbon [J]. Journal of Environmental Engineering, 2012, 6(03): 1010-1014. [2017-08-21].
[11]. RIO S, COQ L L, FAUR C, et al. Preparation of Adsorbents from Sewage Sludge by Steam 7‘Activation for Industrial Emission Treatment[J]. Process Safety & Environmental Protection, 2014, 84(4):258-264.
[12]. TSAI W T, CHANG C Y, LEE S L. A low cost adsorbent from agricultural waste corn cob by zinc chloride activation[J]. Bioresource Technology, 1998, 64 (3): 211-217.
[13]. TSAI W T, CHANG C Y, LEE S L. Preparation and characterization of activated carbons from corn cob[J]. Carbon, 1997, 35(8):1198–1200.
[14]. 马培勇,武晋州,张贤文,等. K2CO3-锯末干混合制备成型活性炭[J/OL]. 过程工程学报, 1-6. (2017-07-12) [2017-08-25].
MA P Y, WU J Z, ZHANG X W, et al, Preparation of formed activated carbon from K2CO3- sawdust dry mixing [J/OL]. Journal of process engineering, 1-6. (2017-07-12) [2017-08-25].
[15]. 尹炳奎. 污泥活性炭吸附剂材料的制备及其在废水处理中的应用[D].上海交通大学,2007.
YIN B K. Preparation of activated carbon adsorbent for sludge and its application in wastewater treatment [D]. Shanghai Jiao Tong University, 2007.
[16]. 苑守瑞, 朱义年, 梁美娜, 等. 氯化锌活化法制备柚子皮活性炭[J]. 环境科学与技术, 2010, 33(s1): 22-25.
YAN S R, ZHU Y N, LIANG M N, et al. Preparation of activated carbon from Shaddock Peel by zinc chloride activation [J]. environmental science and technology, 2010, 33(S1): 22-25
[17]. MOHANTY K, DAS D. BISWAS M N. Preparation and characterization of activated carbons from Sterculia, alata, nutshell by chemical activation with zinc chloride to remove phenol from wastewater[J]. Adsorption-journal of the International Adsorption Society, 2006, 12(2): 119-132.
[18]. 翟云波. 基于化学活化法的污泥衍生吸附剂的制备及应用基础理论研究[D]. 湖南大学, 2005.
ZHAI Y B. Study on Preparation and application of sludge derived adsorbent based on chemical activation method [D]. Hunan University, 2005.
[19]. OZDEMIR I, SAHIN M, ORHAN R, et al. Preparation and characterization of activated carbon from grape stalk by zinc chloride activation[J]. Fuel Processing Technology, 2014, 125(9): 200-206.
[20]. 赵晶晶. 污泥活性炭的制备及其应用研究[D]. 华南理工大学, 2013.
ZHAO J J. Preparation and application of activated sludge from activated sludge [D]. South China University of Technology, 2013
[21]. LIU T, WIE D, ZHANG G, et al. A comparison of flocculent and granular structure of sludge on the influence of activated carbon preparation, characterization and application [J]. Rsc Advances, 2016, 6 (90): 45-52.
[22]. LI Y, LI Y, LI L, et al. Preparation and analysis of activated carbon from sewage sludge and corn stalk[J]. Advanced Powder Technology, 2016, 27(2): 684-691.
[23]. 张会平, 叶李艺, 杨立春. 氯化锌活化法制备木质活性炭研究[C]// 全国活性炭学术研讨会. 2004:42-45.
ZHANG H P, YE L Y, YANG L C. Preparation of woody activated carbon by zinc chloride activation method [C]// Symposium on activated carbon in China. 2004:42-45.
[24]. 陈金妹, 谈萍, 王建永. 气体吸附法表征多孔材料的比表面积及孔结构[J]. 粉末冶金工业, 2011, 21(2):45-49.
CHEN J M, TAN P, WANG Y J. Specific surface area and pore structure of porous materials characterized by gas adsorption method [J]. powder metallurgy industry, 2011, 21 (2): 45-49.
[25]. 孙媛媛. 芦竹活性炭的制备、表征及吸附性能研究[D]. 山东大学, 2014.
SUN Y Y, Gian treed activated carbon preparation, characterization and adsorption properties of [D]. Shandong University, 2014
[26]. 邢献军, 孙宗康, 范方宇,等. 干法制备高中孔率生物质成型活性炭[J/OL]. 化工学报, 2016, 67(06): 2638-2644. (2016-04-05) [2017-08-25]
XING X J, SUN Z K, FANG F Y, et al, Preparation of activated carbon from biomass with high porosity rate by dry process [J/OL]. Journal of chemical engineering, 2016, 67(06): 2638-2644. (2016-04-05) [2017-08-25]
[27]. WARNOCK D D, LEHMANN J, KUYPER T W, et al. Mycorrhizal responses to biochar in soil concepts and mechanisms[J]. Plant & Soil, 2007, 300(2): 9-20.
[28]. 赵兴兴, 王哲. 氧氟沙星在碳纳米管上的吸附机制研究[J]. 环境科学, 2014, 35(2): 663-668.
ZHAO X X, WANG Z, Study on the adsorption mechanism of ofloxacin on carbon nanotubes [J]. environmental science, 2014, 35(2): 663-668.
[29]. 郭文娟, 梁学峰, 林大松,等. 土壤重金属钝化修复剂生物炭对镉的吸附特性研究[J]. 环境科学, 2013, 34(9): 3716-3721.
GUO W J, LIANG X F, LIN D S, et al. Heavy metal adsorption characteristics of soil remediation [J]. environmental science, biological carbon agent on CD, 2013, 34(9): 3716-3721.
[30]. YANG H, XU R, XUE X, et al. Hybrid surfactant-templated mesoporous silica formed in ethanol and its application for heavy metal removal[J]. Journal of Hazardous Materials, 2008, 152(2): 690-698.

污泥-锯末混合ZnCl₂活化制备活性炭

Preparation of activated carbon from sludge and sawdust with ZnCl₂ as activator

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

[1]	赵晓腾周新涛罗中秋韦宇兰雄陆艳. 二氧化钛基复合材料对常见染料的去除性能及其机理研究进展[J]. 过程工程学报, 2022, 22(9): 1169-1180.
[2]	兰雄刘钦周新涛罗中秋赵晓腾陆艳. 吸附法脱除废水中四环素的研究进展[J]. 过程工程学报, 2022, 22(8): 989-1000.
[3]	陶润萍董伟强胡庆松朱靖王智鑫徐轶群. Brij30/β-FeOOH/GO复合材料的可控构筑及其对盐酸四环素吸附性能[J]. 过程工程学报, 2022, 22(7): 979-988.
[4]	韩娟方思含黄文睿吴嘉聪李媛媛王蕾毛艳丽王赟. 泡沫分离设备的研究进展[J]. 过程工程学报, 2022, 22(7): 839-852.
[5]	聂发辉吴道黄慧倩徐志威吴钦刘占孟. Fe3O4@SA/CTS凝胶球对亚甲基蓝及碱性品红的吸附[J]. 过程工程学报, 2022, 22(6): 734-744.
[6]	蔡铖张海燕王英付海阔黄玲唐仁衡肖方明. 锂离子电池高镍三元正极材料LiNi_0.8Co_0.1Mn_0.1O₂的性能研究[J]. 过程工程学报, 2022, 22(6): 754-763.
[7]	冯凡曾坚贤黄小平张锐吴振威. 沸石咪唑骨架膜的制备及其应用进展[J]. 过程工程学报, 2022, 22(6): 709-719.
[8]	肖邦曹青马培勇毕海林李鹏程. 基于分子动力学模拟的羟基改性调控活性炭对甲苯吸附性能的作用机理研究[J]. 过程工程学报, 2022, 22(5): 660-670.
[9]	仪凡贺鹏曹俊雅曹妍王利国陈家强李会泉. CaY分子筛对乙二醇和1,2-丁二醇吸附分离性能的研究[J]. 过程工程学报, 2022, 22(4): 448-457.
[10]	李燕郭昌进丁磊. 磁性离子交换树脂强化水源中有机物去除性能研究[J]. 过程工程学报, 2022, 22(4): 542-551.
[11]	杜含笑季娟秦辰伟张泽李锋锋沈毅. g-C₃N₄制备方法及其光催化性能提升途径的研究进展[J]. 过程工程学报, 2022, 22(2): 162-175.
[12]	张亚卓战金辉. CH₃Cl在ZnO(001)和ZnO(100)表面吸附的第一性原理计算[J]. 过程工程学报, 2022, 22(2): 240-248.
[13]	胡美清金伟. 电吸附-电沉积联合作用下的低浓度铜离子分离[J]. 过程工程学报, 2021, 21(8): 976-984.
[14]	李小亮, 田国才. 盐酸在黄铜矿表面吸附机制的第一性原理计算[J]. 过程工程学报, 2021, 21(7): 836-846.
[15]	张智霖, 丁磊, 周强, 余剑, 郭昌进, 张德伟. 响应曲面法优化木薯酒精污泥基活性炭制备及对没食子酸的吸附性能[J]. 过程工程学报, 2021, 21(7): 794-806.