Leaching Behaviors of Heavy Metals from Electric Furnace Refining Slag in Different Solutions

MA Chi LI Hui-quan WANG Chen-ye BAO Wei-jun XU De-hua LIAO Dan-kui HUANG Ke-lin   

  1. College of Chemistry and Chemical Engineering, Cuangxi University Institute of Process Engineering, Chinese Academy of Sciences Institute of Process Engineering, Chinese Academy of Sciences Institute of Process Engineering, Chinese Academy of Sciences Institute of Process Engineering, Chinese Academy of Sciences School of Chemistry and Chemical Engineering, Guangxi University, Nanning Guangxi Branch of China Academy of Science and Technology Development
  • Received:2015-01-27 Revised:2015-03-31 Online:2015-06-20 Published:2015-06-20
  • Contact: MA Chi

PDF

被引次数

1

摘要： 采用全溶实验、短期与长期浸出实验，对电炉精炼渣中重金属元素的浸出行为进行研究，并通过SEM与XRD分析其机理. 结果表明，电炉精炼渣中Ba元素短期浸出浓度最高值为52.10 mg/L，超出国家污水重金属排放标准；Ni元素短期浸出浓度最高值为0.025 mg/L，V元素长期浸出浓度最高值为0.176 mg/L，超出生活饮用水卫生标准. 重金属元素的浸出主要是由于钢渣中Ca2SiO4×H2O (C-S-H)等结构的破坏.

关键词: 电炉精炼渣, 重金属, 浸出

Abstract: The leaching behaviors of heavy metals in electric furnace refining slag were studied by total dissolving, short-term and long-term leaching experiments, and the leaching mechanism was analyzed by SEM and XRD. The results show that in the slag, the concentration of Ba from short-term leaching is higher than the discharge standard of wastewater containing heavy metal, and the concentrations of Ni from short-term leaching and V from long-term leaching are higher than the hygiene standard of domestic and drinking water. Leaching of heavy metals is mainly due to the structural damage of Ca2SiO4×H2O (C-S-H) in the slag.

Key words: electric furnace refining slag, heavy metal, leaching