Ce改性Fe2O3/AC催化剂低温SCR脱硝性能

doi:10.12034/j.issn.1009-606X.217360

摘要/Abstract

摘要： 以活性焦(AC)为载体、Fe和Ce为活性组分，采用等体积浸渍法制备了Fe2O3/AC和Ce?Fe2O3/AC催化剂，研究了Fe含量及Ce掺杂对Fe2O3/AC催化剂低温脱硝性能的影响，并对催化剂进行了表征. 结果表明，当Fe负载量为6wt%时，Fe2O3/AC催化剂的NOx转化率最高，240℃下达93.9%. 掺杂Ce后Ce?Fe2O3/AC催化剂的催化效率明显提高，当质量比Ce:Fe=0.5:6时，NOx转化率较高，120~200℃下NOx转化率比负载6wt% Fe的催化剂提高了5%?20%，且抗硫性能较好，240℃下通入100?10?6(vol) SO2，NOx转化率稳定在94.1%. 掺杂少量Ce可使γ-Fe2O3均匀分散在催化剂表面，且表面吸附氧Oα比例增大，催化剂的还原性增强，促进了选择性催化还原反应进行.

关键词: γ-Fe2O3, Ce, 活性焦, 低温, SCR

Abstract: A series of Fe2O3/AC and Ce?Fe2O3/AC catalysts with activated coke as support, iron and cerium as active ingredients were prepared by impregnation method. The influences of iron and cerium concentrations on the denitrification performance of the Fe2O3/AC catalyst at low temperature were investigated and these catalysts were characterized. The results showed that the Fe2O3/AC catalyst with 6wt% Fe had the best NOx conversion rate of 93.9% at 240℃. The NOx conversion rate using Ce-modified Fe2O3/AC catalyst was obviously improved. When the mass ratio of Ce to Fe was 0.5:6, the NOx conversion rate using Ce?Fe2O3/AC catalyst was higher 5%?20% than that using Fe/AC catalyst with 6wt% Fe at 120~200℃, and it showed a good sulfur resistance. The NOx conversion rate stabilized at 94.1% when the 100?10?6 (vol) SO2 was introduced at 240℃. The γ-Fe2O3 uniformly dispersed on the surface of catalyst after Ce modification, surface-adsorbed oxygen Oα ratio increased and reducibility was good, improving the NOx conversion rate.

Key words: γ-Fe2O3, Ce, Activated coke, Low-temperature, SCR

尹寿来朱宝忠孙运兰訾朝辉陈诚李国波徐天宇. Ce改性Fe₂O₃/AC催化剂低温SCR脱硝性能[J]. 过程工程学报, 2018, 18(3): 509-516.

Shoulai YIN Baozhong ZHU Yunlan SUN Zhaohui ZI Cheng CHEN Guobo LI Tianyu XU. Low-temperature Selective Catalytic Reduction of NOx over Ce-modified Fe2O3/AC Catalysts[J]. Chin. J. Process Eng., 2018, 18(3): 509-516.

参考文献

[1] Qi G, Yang R T. Low-temperature Selective Catalytic Reduction of NO with NH3 over Iron and Manganese Oxides Supported on Titania [J]. Appl. Catal. B Environ., 2003, 44: 217?225.
[2] 彭富昌. 钒系脱硝催化剂的研究现状及发展趋势[J]. 当代化工, 2013, 42: 1562-1564.
Peng F C. Research status and prospect of vanadium catalysts for De-NOx [J]. Contemporary Chemical Industry, 2013, 42: 1562?1564.
[3] 李金虎, 张先龙, 陈天虎, 等. 凹凸棒石负载锰氧化物低温选择性催化还原催化剂的表征及对氨的吸脱附[J]. 催化学报, 2010, 31: 454?460.
Li J H, Zhang X L, Chen T H, et al. Characterization and ammonia adsorption-desorption of palygorskite supported manganese oxide as a low-temperature selective catalytic reduction catalyst [J]. Chinese Journal of Catalysis, 2010, 31: 454?460.
[4] 王学海, 李勇, 刘忠生, 等. 锅炉烟气脱硝工业侧线试验 [J]. 当代化工, 2013, 42: 1485?1488.
Wang X H, Li Y, Liu Z S, et al. Industrial side-line experiment of flue gas denitrification [J]. Contemporary Chemical Industry, 2013, 42: 1485?1488.
[5] Pasel J，Kβner P，Montanari B，et al．Transition metal oxides supported on active carbons as low temperature catalysts for the selective catalytic reduction (SCR) of NO with NH3 [J]. Appl. Catal. B Environ., 1998, 18: 199?213．
[6] 陈九玉, 朱宝忠, 堵同宽, 等. Co改性Fe2O3/AC催化剂低温SCR脱硝性能 [J]. 有色金属工程, 2017, 7: 99-102.
Chen J Y, Zhu B Z, Du T K, et al. Low-temperature selective catalytic reduction of NOx with NH3 over Co modified Fe2O3/AC catalysts [J]. Nonferrous Metals Engineering, 2017, 7: 99?102.
[7] 谢国勇, 刘振宇, 刘有智, 等. 用CuO/γ-Al2O3催化剂同时脱除烟气中的SO2和NO [J]. 催化学报, 2004, 25: 33?38.
Xie G Y, Liu Z Y, Liu Y Z, et al. Simultaneous Removal of SO2 and NO from Flue Gas Using CuO//γ-Al2O3 Catalyst [J], Chinese Journal of Catalysis, 2004, 25: 33?38.
[8] Iwamoto M, Yoda Y, Yamazoe N, et al. Study of metal oxide catalysts by temperature programmed desorption. 4. Oxygen adsorption on various metal oxides [J]. ChemInform., 1978, 10: 2564?2570.
[9] 杨青. Ce改性铁锰复合氧化物低温选择性催化还原NOx研究 [D]. 广州: 华南理工大学, 2011.
Yang Q, Low temperature selective catalytic reduction of NOx over Ce modified FeMnOx catlysts [D]. Guangzhou: South China University of Technology, 2011.
[10] 郭东旭. 新型铁铈钛催化剂SCR脱硝性能及反应动力学研究 [D]. 济南：山东大学, 2013.
Guo D X, Performance and kinetics of the selective catalytic reduction of NOx over novel Fe-Ce-Ti/TiO2 [D]. Jinan: Shandong University, 2013.
[11] 束韫. 铁铈蜂窝金属丝网催化剂用于选择催化还原NOx的研究 [D]. 大连: 大连理工大学, 2013.
Shu Y, Selective catalytic reduction of NOx over Fe?Ce/wire-mesh honeycomb catalyst [D]. Dalian: Dalian University of Technology, 2013.
[12] Mangun C L, Debarr J A, Economy J. Adsorption of sulfur dioxide on ammonia-treated activated carbon fibers[J]. Carbon, 2001, 39: 1689?1696.
[13] Yu Y M, Guo R L, Li C H. Flue gas desulfurization and denitrification performance of the semi-coke adsorbents [J]. J. Fuel Chem. Technol., 2011, 39: 385?389.
[14] Tsuji K, Shiraishi I. Combined desuifurization, denitrification and reduction of air toxics using activated coke: l. Activity of activated coke [J]. Fuel, 1997, 76: 549?553.
[15] 王晓波, 归柯庭. 铁基催化剂低温脱硝性能研究 [J]. 工程热物理学报, 2013, 34: 1671?1674.
Wang X B, Gui K T, Low-temperature selective catalytic reduction of NO with NH3 over iron based catalysts [J]. Journal of Engineering Thermophysics, 2013, 34: 1671?1674.
[16] Liu Z, Wang A, Wang X, et al. Ir-C xerogels synthesized by sol-gel method for NO reduction [J]. Catal. Today, 2008, 137: 162?166.
[17] Maldonado J F, Moreno C, Rivera J, et al. Catalytic graphitization of carbon aerogels by transition metals [J]. Langmuir, 2000, 16: 4367-4373.
[18] Xiang G, Liu S, Yang Z, et al. Physicochemical properties of metal-doped activated carbons and relationship with their performance in the removal of SO2 and NO [J]. J. Hazard. Mater., 2011, 188: 58?66.
[19] 刘炜, 童志权, 罗婕. Ce-Mn/TiO2催化剂选择性催化还原NO的低温活性及抗毒化性能 [J]. 环境科学学报, 2006, 26: 1240?1245.
Liu W, Tong Z Q, Luo J. Low-temperature selective catalytic reduction of NO with NH3 over Ce-Mn/TiO2 catalyst [J]. Acta Scientiae Circumstantiae, 2006, 26: 1240?1245.
[20] 钟标城, 周广英, 王文辉, 等. Fe掺杂对MnOx催化剂结构性质及低温SCR反应机制的影响 [J]. 环境科学学报, 2011, 10: 2091?2101.
Zhong B C, Zhou G Y, Wang W H, et al. The effects of Fe substitution on the structure of MnOx catalyst and reaction pathway for low temperature SCR [J]. Acta Scientiae Circumstantiae, 2006, 26: 1240?1245.
[21] 姜水燕. Fe基分子筛催化剂NH3-SCR性能研究 [D]. 杭州：浙江大学, 2015.
Jiang H Y, Investigation on catalytic performance of Fe-based zeolite catalysts in NH3-SCR [D]. Hangzhou: Zhejiang University. 2015.
[22] Devadas M, Krocher O, Elsener M, et al. Characterization and catalytic investigation of Fe?ZSM5 for urea-SCR [J]. Catal. Today, 2007, 119: 137?-144.
[23] Shen B, Wang F, Liu T. Homogeneous MnOx?CeO2 pellets prepared by a one step hydrolysis process for low-temperature NH3-SCR [J]. Powder Technol., 2014, 253: 152?157.
[24] Gongshin Q, Ralph T Y. Performance and kinetics study for low-temperature SCR of NO with NH3 over MnOx?CeO2 catalyst [J]. J. Catal., 2003, 217: 434?441.
[25] Sun Y, Guo Y, Su W, et al. Low-temperature selective catalytic reduction of NO with NH3 over Fe-Ce-Ox catalysts [J]. Trans. Tianjin Univ., 2017, 23: 35?42.
[26] Zhu L, Zhang L, Qu H, et al. A study on chemisorbed oxygen and reaction process of Fe?CuOx/ZSM-5 via ultrasonic impregnation method for low-temperature NH3-SCR [J]. J. Mol. Catal. A: Chem., 2015, 409: 207?215.
[27] Schindler M, Hawthorne F C, Freund M S, et al. XPS spectra of uranyl minerals and synthetic uranyl compounds. II: The O1s spectrum [J]. Geochim. Cosmochim. Ac., 2009, 73: 2471-2487.
[28] Wu Z B, Jin R B, Liu Y, et al. Ceria modified MnOx/TiO2 as a superior catalyst for NO reduction with NH3 at low?temperature [J]. Cataly. Commun., 2008, 9: 2217?2220.
[29] Brink R W V D, Booneveld S, Pels J R, et al. Catalytic removal of N2O in model flue gases of a nitric acid plant using a promoted Fe zeolite [J]. Appl. Catal. B Environ., 2001, 32: 73?81.
[30] Chen B, Liu N, Liu X, et al. Study on the direct decomposition of nitrous oxide over Fe-beta zeolites: from experiment to theory [J]. Catal. Today, 2011, 175: 245?255.
[31] Mauvezin M, Delahay G, Cop B, et al. Identification of iron species in Fe?BEA: influence of the exchange level [J]. The J. Phys. Chem. B, 2001, 105: 928?935.
[32] Park J H, Choung J H, Nam I S, et al. N2O decomposition over wet? and solid?exchanged Fe-ZSM-5 catalysts [J]. Appl. Catal. B Environ., 2008, 78: 342?-354.
[33] Liu J, Zhao Z, Wang J, et al. The highly active catalysts of nanometric CeO2?supported cobalt oxides for soot combustion [J]. Appl. Catal. B Environ., 2008, 84: 185?195.
[34] 黄增斌, 李翠清, 王振, 等. 不同分子筛负载锰铈催化剂的低温NH3-SCR 脱硝性能 [J]. 燃料化学学报, 2016, 44:1388-1393.
Huang Z B, Li C Q, Wang Z, et al. Performance of Mn?Ce catalysts supported on different zeolites in the NH3?SCR of NOx. Journal of Fuel Chemistry and Technology, 2016, 44: 1388?1393.
[35] Shen B, Ma H, He C, et al. Low temperature NH3-SCR over Zr and Ce pillared clay based catalysts [J]. Fuel Process. Technol., 2014, 119: 121-129.
[36] Sultana A, Sasaki M, Hamada H. Influence of support on the activity of Mn supported catalysts for SCR of NO with ammonia [J]. Catal. Today, 2012, 185: 284-289.
[37] 庄柯, 裘婧, 许波连, 等. NO选择性催化还原Ce?Mn?Ti?O催化剂铈组分助催化作用 [J]. 物理化学学报, 2012, 28: 681?685.
Zhuang K, Qiu J, Xu B L, et al. Promotional Effect of Cerium Oxide on the Catalytic Properties of Ce?Mn?Ti?O Catalysts for Selective Catalytic Reduction of NO [J]. Acta Physico-Chimica Sinica, 2012, 28: 681?685.

Ce改性Fe₂O₃/AC催化剂低温SCR脱硝性能

Low-temperature Selective Catalytic Reduction of NOx over Ce-modified Fe2O3/AC Catalysts

PDF

可视化

摘要/Abstract

引用本文

使用本文

参考文献

相关文章 15

编辑推荐

Metrics

[1]	徐家明皇甫林史玉婷郭洪范高士秋李长明余剑. 低温烟气脱硝催化剂制备工艺及性能探究[J]. 过程工程学报, 2022, 22(7): 863-872.
[2]	林振浩李军业金志江钱锦远. LNG接收站用低温球阀阀座唇形密封圈接触特性分析[J]. 过程工程学报, 2022, 22(6): 819-827.
[3]	申展江志东张鹏飞张子瑜车海英马紫峰. 低温甲醇水重整制氢催化剂研究进展[J]. 过程工程学报, 2022, 22(5): 573-585.
[4]	万琼任迎春赵志啸张新艳王文静郝婧羽黎璇鞠恺. 温度/pH双响应硝化菌凝胶球的制备及特性研究[J]. 过程工程学报, 2021, 21(11): 1346-1354.
[5]	向杰张松平张贵锋罗坚余蓉. 一步离子交换层析从Cohn组分V上清液中分离人血清白蛋白[J]. 过程工程学报, 2021, 21(1): 92-99.
[6]	于凤芹李运甲刘周恩李文松张卫东高士秋许光文余剑. 移动床活性焦烟气净化工艺中废活性焦的形成与特征分析[J]. 过程工程学报, 2020, 20(6): 695-702.
[7]	王殿二王玲高国龙徐新吴鹏张亚平. Ce-Fe/ZSM-5催化剂用于燃机烟气SCR脱硝的性能[J]. 过程工程学报, 2020, 20(6): 718-727.
[8]	王来勇钱付平朱景晶黄乃金徐兵吴昊. 选择性催化还原蜂窝状催化剂内流动特性的多尺度模拟[J]. 过程工程学报, 2020, 20(2): 133-140.
[9]	熊浩包雨云汪晶蔡子琦. 具有黏结颗粒的搅拌槽功率特性[J]. 过程工程学报, 2020, 20(11): 1273-1280.
[10]	武文粉李会泉孟子衡王晨晔王兴瑞赵晨. 碱溶法回收废SCR脱硝催化剂中的二氧化钛[J]. 过程工程学报, 2019, 19(S1): 72-80.
[11]	何辉祁贵生刘有智郑奇任慧云. 超重力强化干法脱硝制氨工艺[J]. 过程工程学报, 2019, 19(4): 845-852.
[12]	宁汝亮刘霄龙朱廷钰. 低温SCR脱硝催化剂研究进展[J]. 过程工程学报, 2019, 19(2): 223-234.
[13]	潘博王露雨王海军江松达万里强郝旭峰田杰黄发荣. 聚三唑酯树脂的合成及其性能[J]. 过程工程学报, 2019, 19(1): 181-188.
[14]	张浩徐远迪刘秀玉. 优化制备粒度均匀分布的Ce-Cu/TiO₂空心微球及其光–湿性能[J]. 过程工程学报, 2019, 19(1): 195-201.
[15]	赵长多范美玲杨晓博胡文斌夏启斌. 纳米零价铁对水溶液中钒离子的吸附性能[J]. 过程工程学报, 2018, 18(6): 1253-1260.